Publikationen

In situ forming hydrogels with catechol groups as tissue reactive functionalities are interesting bioinspired materials for tissue adhesion. Poly(ethylene glycol) (PEG)–catechol tissue glues have been intensively investigated for this purpose. Different cross-linking mechanisms (oxidative or metal complexation) and cross-linking conditions (pH, oxidant concentration, etc.) have been studied in order to optimize the curing kinetics and final cross-linking degree of the system. However, reported systems still show limited mechanical stability, as expected from a PEG network, and this fact limits their potential application to load bearing tissues. Here, we describe mechanically reinforced PEG–catechol adhesives showing excellent and tunable cohesive properties and adhesive performance to tissue in the presence of blood. We used collagen/PEG mixtures, eventually filled with hydroxyapatite nanoparticles. The composite hydrogels show far better mechanical performance than the individual components. It is noteworthy that the adhesion strength measured on skin covered with blood was >40 kPa, largely surpassing (>6 fold) the performance of cyanoacrylate, fibrin, and PEG–catechol systems. Moreover, the mechanical and interfacial properties could be easily tuned by slight changes in the composition of the glue to adapt them to the particular properties of the tissue. The reported adhesive compositions can tune and improve cohesive and adhesive properties of PEG–catechol-based tissue glues for load-bearing surgery applications

The exploitation of easily accessible and nontoxic natural catechol compounds for surface functionalization and coating is attracting growing interest for biomedical applications. We report herein the deposition on different substrates of chemically stable thin films by autoxidation of 1 mM caffeic acid (CA) solutions at pH 9 in the presence of equimolar amounts of hexamethylenediamine (HMDA). UV–visible, mass spectrometric, and solid state 13C and 15N NMR analysis indicated covalent incorporation of the amine during CA polymerization to produce insoluble trioxybenzacridinium scaffolds decorated with carboxyl and amine functionalities. Similar coatings are obtained by replacing CA with 4-methylcatechol (MC) in the presence of HMDA. No significant film deposition was detected in the absence of HMDA nor by replacing it with shorter chain ethylenediamine, or with monoamines. The CA/HMDA-based films resisted oxidative and reductive treatments, displayed efficient Fe(II) and Cu(II) binding capacity and organic dyes adsorption, and provided an excellent cytocompatible platform for growing embryonic stem cells. These results pointed to HMDA as an efficient cross-linking mediator of film deposition from natural catechols for surface functionalization and coatings.

Cell adhesion is studied on multivalent knottins, displaying RGD ligands with a high affinity for integrin receptors, that are assembled on CB[8]-methylviologen-modified surfaces. The multivalency in the knottins stems from the number of tryptophan amino acid moieties, between 0 and 4, that can form a heteroternary complex with cucurbit[8]uril (CB[8]) and surface-tethered methylviologen (MV2+). The binding affinity of the knottins with CB[8] and MV2+ surfaces was evaluated using surface plasmon resonance spectroscopy. Specific binding occurred, and the affinity increased with the valency of tryptophans on the knottin. Additionally, increased multilayer formation was observed, attributed to homoternary complex formation between tryptophan residues of different knottins and CB[8]. Thus, we were able to control the surface coverage of the knottins by valency and concentration. Cell experiments with mouse myoblast (C2C12) cells on the self-assembled knottin surfaces showed specific integrin recognition by the RGD-displaying knottins. Moreover, cells were observed to elongate more on the supramolecular knottin surfaces with a higher valency, and in addition, more pronounced focal adhesion formation was observed on the higher-valency knottin surfaces. We attribute this effect to the enhanced coverage and the enhanced affinity of the knottins in their interaction with the CB[8] surface. Collectively, these results are promising for the development of biomaterials including knottins via CB[8] ternary complexes for tunable interactions with cells.

Biomimetic and stimuli-responsive cell-material interfaces are actively being developed to study and control various cell-dynamics phenomena. Since cells naturally reside in the highly dynamic and complex environment of the extracellular matrix, attempts are being made to replicate these conditions in synthetic biomaterials. Supramolecular chemistry, dealing with noncovalent interactions, has recently provided possibilities to incorporate such dynamicity and responsiveness in various types of architectures. Using a cucurbit[8]uril-based host–guest system, we have successfully established a dynamic and electrochemically responsive interface for the display of the integrin-specific ligand, Arg-Gly-Asp (RGD), to promote cell adhesion. Due to the weak nature of the noncovalent forces by which the components at the interface are held together, we expected that cell adhesion would also be weaker in comparison to traditional interfaces where ligands are usually immobilized by covalent linkages. To assess the stability and limitations of our noncovalent interfaces, we performed single-cell force spectroscopy studies using fluid force microscopy. This technique enabled us to measure rupture forces of multiple cells that were allowed to adhere for several hours on individual substrates. We found that the rupture forces of cells adhered to both the noncovalent and covalent interfaces were nearly identical for up to several hours. We have analyzed and elucidated the reasons behind this result as a combination of factors including the weak rupture force between linear Arg-Gly-Asp and integrin, high surface density of the ligand, and increase in effective concentration of the supramolecular components under spread cells. These characteristics enable the construction of highly dynamic biointerfaces without compromising cell-adhesive properties.

Stacked-layer heterostructure films of 2D thiophene nanosheets and electrochemically exfoliated graphene are constructed for ultrahigh-rate all-solid-state flexible pseudocapacitors and micro-supercapacitors with superior volumetric capacitance due to the synergetic effect of the ultrathin pseudocapacitive thiophene nanosheets and the capacitive electrochemically exfoliated graphene.

Biological materials achieve directional reinforcement with oriented assemblies of anisotropic building blocks. One such example is the nanocomposite structure of keratinized epithelium on the toe pad of tree frogs, in which hexagonal arrays of (soft) epithelial cells are crossed by densely packed and oriented (hard) keratin nanofibrils. Here, a method is established to fabricate arrays of tree-frog-inspired composite micropatterns composed of polydimethylsiloxane (PDMS) micropillars embedded with polystyrene (PS) nanopillars. Adhesive and frictional studies of these synthetic materials reveal a benefit of the hierarchical and anisotropic design for both adhesion and friction, in particular, at high matrix–fiber interfacial strengths. The presence of PS nanopillars alters the stress distribution at the contact interface of micropillars and therefore enhances the adhesion and friction of the composite micropattern. The results suggest a design principle for bioinspired structural adhesives, especially for wet environments.

Novolac-derived nanoporous carbon beads were used as conductive matrix for lithium-sulfur battery cathodes. We employed a facile self-emulsifying synthesis to obtain sub-micrometer novolac-derived carbon beads with nanopores. After pyrolysis, the carbon beads showed already a specific surface area of 640 m2 g−1 which was increased to 2080 m2 g−1 after physical activation. The non-activated and the activated carbon beads represent nanoporous carbon with a medium and a high surface area, respectively. This allows us to assess the influence of the porosity on the electrochemical performance of lithium-sulfur battery cathodes. The carbon/sulfur hybrids were obtained from two different approaches of sulfur infiltration: melt-infusion of sulfur (annealing) and in situ formation of sulfur from sodium thiosulfate. The best performance (∼880 mAh gsulfur−1 at low charge rate; 5th cycle) and high performance stability (>600 mAh gsulfur−1 after 100 cycles) were found for the activated carbon beads when using melt infusion of sulfur.

Intercalation-induced dimensional changes in a composite battery electrode (comprising a polymeric binder) are one of the major factors limiting electrode cycling performance. Since electrode performance is expressed by the quantities averaged over its entire surface area (e.g., capacity retention, Faradaic efficiency, rate capability), significant efforts have been made to develop a methodology allowing its facile mechanical diagnostics at the same areal scale. Herein we introduce such a generic methodology for a highly sensitive in situ monitoring of intrinsic mechanical properties of composite battery electrodes. The gravimetric, dimensional, viscoelastic, and adhesive changes in the composite electrodes caused by Li-ions intercalation are assessed noninvasively and in real time by electrochemical quartz-crystal microbalance with dissipation monitoring (EQCM-D). Multiharmonic acoustic waves generated by EQCM-D penetrate into thin porous electrodes comprising either rigid or a soft binder resulting in frequency and dissipation changes quantified by analytical acoustic load impedance models. As a first demonstration, we used a composite LiFePO4 (LFP) electrode containing either polyvinylidene dichloride (PVdF) or Na carboximethyl cellulose (NaCMC) as rigid and viscoelastic binders, respectively, in aqueous electrolytes. The intercalation-induced volume changes of LFP electrode were evaluated from a hydrodynamic correction to the mass effect of the intercalated ions for PVdF, and both components of the effective complex shear modulus (i.e., storage and loss moduli) in case of NaCMC binder have been extracted. The sliding friction coefficients for large particles bound at their bottom to the quartz crystal surface (a measure of the adhesion strength of binders) has also been evaluated. Tracking the mechanical properties of the composite electrodes in different environments and charging/cycling conditions in a self-consistent manner provides all necessary conditions for an optimal selection of the polymeric binders resistant to intercalation-induced volume changes of intercalation particles.

In this study, atomic layer deposition (ALD) is employed to synthesize hybrid electrode materials of especially tailored mesoporous carbon and vanadium oxide. The highly conformal and precise character of ALD allowed for depositing up to 65 mass % of vanadium oxide inside the 5–20 nm mesopores of the carbon particles, without substantially obstructing internal surface area. The deposited phase was identified as orthorhombic V2O5, and an increasing crystalline order was detected for higher mass loadings. Employing the hybrid material as lithium and sodium intercalation hosts at a rate of 0.5C yielded specific capacities of 310 and 250 mAh/g per V2O5, respectively, while showing predominantly pseudocapacitive behavior, that is, capacitor-like voltage profiles. C-rate benchmarking revealed a retention of about 50% of the maximum capacity for both lithium and sodium at a high rate of 100C. When testing for longevity in lithium-containing electrolyte, a steadily increasing capacity was observed to 116% of the initial value after 2000 cycles. In sodium electrolyte, the capacity faded to 75% after 2000 cycles, which represents one of the most stable performances for sodium intercalation in the literature. Homogeneously distributed vanadium oxide that is locally confined in the tailored carbon mesopores was identified as the reason for enhanced cyclability and rate behavior of the hybrid material.

Atomic layer deposition has proven to be a particularly attractive approach for decorating mesoporous carbon substrates with redox active metal oxides for electrochemical energy storage. This study, for the first time, capitalizes on the cyclic character of atomic layer deposition to obtain a highly conformal and atomically controlled decoration of carbon onions with alternating stacks of vanadia and titania. The addition of 25 mass% TiO2 leads to an expansion of the VO2 unit cell, thus greatly enhancing lithium intercalation capacity and kinetics. Electrochemical characterization revealed ultrahigh discharge capacity of up to 382 mAh[middle dot]g-1 of the composite electrode (554 mAh[middle dot]g-1 per metal oxide) with an impressive capacity retention of 82 mAh[middle dot]g-1 (120 mAh[middle dot]g-1 per metal oxide) at a high discharge rate of 20 A[middle dot]g-1 or 52 C. Rigorous stability benchmarking showed superior stability over 3,000 cycles when discharging to a reduced potential of -1.8 V vs. carbon. These capacity values are among the highest reported for any metal oxide system, while in addition, supercapacitor-like power performance and longevity are achieved. On a device level, high specific energy and power of up to 110 Wh[middle dot]kg-1 and 6 kW[middle dot]kg-1, respectively, were achieved when employing the hybrid material as anode versus activated carbon cathode.