Scientific publications

Patterned microstructures represent a potential approach for improving current wound closure strategies. Microstructures can be fabricated by multiple techniques including replica molding of soft polymer-based materials. However, polymeric microstructures often lack the required shear resistance with tissue needed for wound closure. In this work, scalable microstructures made from composites based on polydimethylsiloxane (PDMS) were explored to enhance the shear resistance with wet tissue. To achieve suitable mechanical properties, PDMS was reinforced by incorporation of polyethylene (PE) particles into the pre-polymer and by coating PE particle reinforced substrates with parylene. The reinforced microstructures showed a 6-fold enhancement, the coated structures even a 13-fold enhancement in Young׳s modulus over pure PDMS. Shear tests of mushroom-shaped microstructures (diameter 450 µm, length 1 mm) against chicken muscle tissue demonstrate first correlations that will be useful for future design of wound closure or stabilization implants.

The two-way shape-memory effect (TWSME) in Nickel–titanium (NiTi) alloys is of interest for applications in aerospace, biomedicine, and microengineering due to its reversible shape recovery. In this study, the authors demonstrate two approaches to obtain switchable surface structures using the TWSME. Samples are structured using two surface geometries by either cold embossing, or pulse electrochemical machining (PECM). After planarization, a change from optically smooth to structured and vice versa is observed. The switch is induced through heating and cooling the sample above and below the phase transformation temperature. The protrusions reflect the pattern applied by the two processes. Both methods are promising for preparation of switchable metallic surfaces on larger areas.

Biologically inspired, fibrillar dry adhesives continue to attract much attention as they are instrumental for emerging applications and technologies. To date, the adhesion of micropatterned gecko-inspired surfaces has predominantly been tested on stiff, smooth substrates. However, all natural and almost all artificial surfaces have roughnesses on one or more different length scales. In the present approach, micropillar-patterned PDMS surfaces with superior adhesion to glass substrates with different roughnesses are designed and analyzed. The results reveal for the first time adhesive and nonadhesive states depending on the micropillar geometry relative to the surface roughness profile. The data obtained further demonstrate that, in the adhesive regime, fibrillar gecko-inspired adhesive structures can be used with advantage on rough surfaces; this finding may open up new applications in the fields of robotics, biomedicine, and space exploration.

Whole cells can be studied in their native liquid environment using electron microscopy, and unique information about the locations and stoichiometry of individual membrane proteins can be obtained from many cells thus taking cell heterogeneity into account. Of key importance for the further development of this microscopy technology is knowledge about the effect of electron beam radiation on the samples under investigation. We used environmental scanning electron microscopy (ESEM) with scanning transmission electron microscopy (STEM) detection to examine the effect of radiation for whole fixed COS7 fibroblasts in liquid. The main observation was the localization of nanoparticle labels attached to epidermal growth factor receptors (EGFRs). It was found that the relative distances between the labels remained mostly unchanged (<1.5%) for electron doses ranging from the undamaged native state at 10 e−/Å2 toward 103 e−/Å2. This dose range was sufficient to determine the EGFR locations with nanometer resolution and to distinguish between monomers and dimers. Various different forms of radiation damage became visible at higher doses, including severe dislocation, and the dissolution of labels.

Background: Quantum dots (QDs) have great potential as fluorescent labels but cytotoxicity relating to extra- and intracellular degradation in biological systems has to be addressed prior to biomedical applications. In this study, human intestinal cells (Caco-2) grown on transwell membranes were used to study penetration depth, intracellular localization, translocation and cytotoxicity of CdSe/ZnS QDs with amino and carboxyl surface modifications. The focus of this study was to compare the penetration depth of QDs in differentiated vs undifferentiated cells using confocal microscopy and image processing.
Results: Caco-2 cells were exposed to QDs with amino (NH2) and carboxyl (COOH) surface groups for 3 days using a concentration of 45 µg cadmium ml−1. Image analysis of confocal/multiphoton microscopy z-stacks revealed no penetration of QDs into the cell lumen of differentiated Caco-2 cells. Interestingly, translocation of cadmium ions onto the basolateral side of differentiated monolayers was observed using high resolution inductively coupled plasma mass spectrometry (ICP-MS). Membrane damage was neither detected after short nor long term incubation in Caco-2 cells. On the other hand, intracellular localization of QDs after exposure to undifferentiated cells was observed and QDs were partially located within lysosomes.Conclusions: In differentiated Caco-2 monolayers, representing a model for small intestinal enterocytes, no penetration of amino and carboxyl functionalized CdSe/ZnS QDs into the cell lumen was detected using microscopy analysis and image processing. In contrast, translocation of cadmium ions onto the basolateral side could be detected using ICP-MS. However, even after long term incubation, the integrity of the cell monolayer was not impaired and no cytotoxic effects could be detected. In undifferentiated Caco-2 cells, both QD modifications could be found in the cell lumen. Only to some extend, QDs were localized in endosomes or lysosomes in these cells. The results indicate that the differentiation status of Caco-2 cells is an important factor in internalization and localization studies using Caco-2 cells. Furthermore, a combination of microscopy analysis and sensitive detection techniques like ICP-MS are necessary for studying the interaction of cadmium containing QDs with cells.

Copper indium gallium diselenide (CIGS) nanoparticles are one the promising materials for solar cell technology applications. In this study, CIGS nanostructures were synthesized using a solvothermal method. By adding different ammonium salts, the synthesis time could be reduced by up to 2 h compared to the routine solvothermal method. The effects of ammonium halides on the synthesis process and on particle growth were investigated. Structural properties and size information of the synthesized nanoparticles were obtained by X-ray diffraction and transmission electron microscopy. The CIGS particles were found to be tetragonal with average sizes ranging from 20 to 100 nm. The optical band gap of these structures was found 1.38 and 1.46 eV. Shortening the synthesis time of dispersed CIGS nanoparticles could be interesting for the development of cost-effective or non-vacuum technologies.

The oxides of the transition metal molybdenum exhibit excellent antimicrobial properties. We present the preparation of molybdenum trioxide dihydrate (MoO3 × 2H2O) by an acidification method and demonstrate the thermal phase development and morphological evolution during and after calcination from 25 °C to 600 °C. The thermal dehydration of the material was found to proceed in two steps. Microbiological roll-on tests using Staphylococcus aureus, Escherichia coli and Pseudomonas aeruginosa were performed and exceptional antimicrobial activities were determined for anhydrous samples with orthorhombic lattice symmetry and a large specific surface area. The increase in the specific surface area is due to crack formation and to the loss of the hydrate water after calcination at 300 °C. The results support the proposed antimicrobial mechanism for transition metal oxides, which based on a local acidity increase as a consequence of the augmented specific surface area.

Datasets from a slow carbonate vapor diffusion and mineral precipitation protocol for Dictyostelium ECM and cellulose stalks show examples for composite materials obtained by an in vitro approach, which differs substantially from the in vivo approach reported in The Journal of Structural Biology, doi: 10.1016/j.jsb.2016.03.015 [1]. Methods for obtaining the datasets include bright field transmitted light microscopy, fluorescence microscopy, LC-PolScope birefringence microscopy, variable pressure scanning electron microscopy (VP-SEM/ESEM), and Raman imaging spectroscopy.

Proteins are known to play various key roles in the formation of complex inorganic solids during natural biomineralisation processes. However, in most cases our understanding of the actual underlying mechanisms is rather limited. One interesting example is perlucin, a protein involved in the formation of nacre, where it is believed to promote the crystallisation of calcium carbonate. In the present work, we have used potentiometric titration assays to systematically investigate the influence of recombinant GFP-labeled perlucin derivatives on the early stages of CaCO3 formation. Our results indicate that different parts of the protein can impact nucleation in distinct ways and act in either a retarding or promoting fashion. The most important finding is that full-length GFP-perlucin changes the nature of the initially precipitated phase and seems to favour the direct formation of crystalline polymorphs over nucleation of ACC and subsequent phase transformation, as observed in reference experiments without protein. This confirms the supposed role of perlucin in nacre biomineralisation and may rely on specific interactions between the protein and the crystal lattice of the emerging mineral phase.