Scientific publications

The authors develop a protective transparent coating of aluminum oxide through direct oxidation of aluminum-coated glass. Aluminum coatings are deposited on low-iron glass substrates using a physical deposition method and then oxidized at different temperatures. A uniform nano-porous structure with grain sizes of approximately 30–80 nm is observed. X-ray diffraction, TEM images, and EDX analysis indicate the formation of crystalline γ-Al2O3, Si, and stishovite-SiO2 as a result of interdiffusion. The samples treated at different temperatures have hardness values ranging from 5 to 9 H, which is within the desirable range for industrial scratch-resistant coatings. The optical transmission of around 75–85% at visible wavelengths makes the proposed technique useful for the design of protective transparent coatings.

Coating on large surfaces is a critical issue in both academic studies and industrial production. This work proposes a novel method of coating a large flat substrate (50 × 100 cm2) via a wet chemical process using a very small amount (20 ml) of coating solution. The sol material consisted of surface-modified silicon dioxide (SiO2) nanoparticles (10–30 nm), which have the optimal antireflective (AR) function in the visible spectral range for thin films with a thickness ranging from 110 to 120 nm. Ellipsometry results demonstrate a homogeneous thickness of the AR coating on glass (109.4 ± 2.7 nm). A deviation of less than 3% over a large coated surface was observed. Crack-free coatings with homogeneous morphology on the surface of the coatings were observed using scanning electron microscopy. The AR effect was confirmed with UV–vis measurements, with an average transmittance of 91.1% and 94.7%, respectively, in visible wavelengths for the one-sided and double-sided AR coatings (in comparison to 88% for uncoated glass).

There is great technological interest in elucidating the effect of particle size on the luminescence efficiency of doped rare earth oxides. This study demonstrates unambiguously that there is a size effect and that it is not dependent on the calcination temperature. The Y2O3:Eu and Gd2O3:Eu particles used in this study were synthesized using wet chemistry to produce particles ranging in size between 7 nm and 326 nm and a commercially available phosphor. These particles were characterized using three excitation methods: UV light at 250 nm wavelength, electron beam at 10 kV, and X-rays generated at 100 kV. Regardless of the excitation source, it was found that with increasing particle diameter there is an increase in emitted light. Furthermore, dense particles emit more light than porous particles. These results can be explained by considering the larger surface area to volume ratio of the smallest particles and increased internal surface area of the pores found in the large particles. For the small particles, the additional surface area hosts adsorbates that lead to non-radiative recombination, and in the porous particles, the pore walls can quench fluorescence. This trend is valid across calcination temperatures and is evident when comparing particles from the same calcination temperature.

Introducing novel shapes to particulate carrier systems adds unique features to modern drug and gene delivery. Depending on the route of administration, particle geometry can influence deposition and fate within biological environments. In this work, a template-assisted engineering technique is applied, providing full control of size and shape in the preparation of aspherical, nanostructured microparticles. Based on the interconnection of nanoparticles, stabilized by a functional layer-by-layer (LbL) coating, the resulting cylindrical micrometer architecture is especially qualified for pulmonary delivery. Designed as gene delivery system, plasmid-DNA (pCMV-luciferase) and branched polyethylenimine are used to reach both structural integrity of the carrier system and delivery of genes into the cells of interest. Due to their size, particles are exclusively taken up by phagocytes, which also adds a targeting effect to the introduced system. The luciferase expression is demonstrated in macrophages showing increasing levels over a time period of at least 7 d. Furthermore, it is shown for the first time that the expression is depending on the LbL design. From in vivo experiments, corresponding luciferase expression is observed in mice alveolar macrophages. Combining site specific transport with the possibility of genetically engineering immunocompetent phagocytes, the presented system offers promising potential to improve applications for cell-based immunotherapy.

Iron is an essential growth determinant for plants, and plants acquire this micronutrient in amounts they need in their environment. Plants can increase iron uptake in response to a regulatory transcription factor cascade. Arabidopsis thaliana serves as model plant to identify and characterize iron regulation genes. Here, we show that overexpression of subgroup Ib bHLH transcription factor bHLH039 (39Ox) caused constitutive iron acquisition responses, which resulted in enhanced iron contents in leaves and seeds. Transcriptome analysis demonstrated that 39Ox plants displayed simultaneously gene expression patterns characteristic of iron deficiency and iron stress signaling. Thereby, we could dissect iron deficiency response regulation. The transcription factor FIT, which is required to regulate iron uptake, was essential for the 39Ox phenotype. We provide evidence that subgroup Ib transcription factors are involved in FIT transcriptional regulation. Our findings pose interesting questions to the feedback control of iron homeostasis.

Summary Engineering of biomaterials with specific biological properties has gained momentum as a means to control stem cell behavior. Here, we address the effect of bifunctionalized hydrogels comprising polylysine (PL) and a 19-mer peptide containing the laminin motif IKVAV (IKVAV) on embryonic and adult neuronal progenitor cells under different stiffness regimes. Neuronal differentiation of embryonic and adult neural progenitors was accelerated by adjusting the gel stiffness to 2 kPa and 20 kPa, respectively. While gels containing IKVAV or PL alone failed to support long-term cell adhesion, in bifunctional gels, IKVAV synergized with PL to promote differentiation and formation of focal adhesions containing β1-integrin in embryonic cortical neurons. Furthermore, in adult neural stem cell culture, bifunctionalized gels promoted neurogenesis via the expansion of neurogenic clones. These data highlight the potential of synthetic matrices to steer stem and progenitor cell behavior via defined mechano-adhesive properties.

Biomaterials for cell culture allowing simple and quantitative presentation of instructive cues enable rationalization of the interplay between cells and their surrounding microenvironment. Poly(acrylamide) (PAAm) hydrogels are popular 2D-model substrates for this purpose. However, quantitative and reproducible biofunctionalization of PAAm hydrogels with multiple ligands in a trustable, controlled, and independent fashion is not trivial. Here, we describe a method for bifunctional modification of PAAm hydrogels with thiol- and amine- containing biomolecules with controlled densities in an independent, orthogonal manner. We developed copolymer networks of AAm with 9% acrylic acid and 2% N-(4-(5-(methylsulfonyl)-1,3,4-oxadiazol-2-yl)phenyl)acrylamide. The covalent binding of thiol- and amine-containing chromophores at tunable concentrations was demonstrated and quantified by UV spectroscopy. The morphology, mechanical properties, and homogeneity of the copolymerized hydrogels were characterized by scanning electron microscopy, dynamic mechanical analysis, and confocal microscopy studies. Our copolymer hydrogels were bifunctionalized with polylysine and a laminin-mimetic peptide using the specific chemistries. We analyzed the effect of binding protocol of the two components in the maturation of cultured postmitotic cortical neurons. Our substrates supported neuronal attachment, proliferation, and neuronal differentiation. We found that neurons cultured on our hydrogels bifunctionalized with ligand-specific chemistries in a sequential fashion exhibited higher maturation at comparable culture times than using a simultaneous bifunctionalization strategy, displaying a higher number of neurites, branches, and dendritic filopodia. These results demonstrate the relevance of quantitative and optimized coupling chemistries for the performance of simple biomaterials and with sensitive cell types.

In situ forming hydrogels with catechol groups as tissue reactive functionalities are interesting bioinspired materials for tissue adhesion. Poly(ethylene glycol) (PEG)–catechol tissue glues have been intensively investigated for this purpose. Different cross-linking mechanisms (oxidative or metal complexation) and cross-linking conditions (pH, oxidant concentration, etc.) have been studied in order to optimize the curing kinetics and final cross-linking degree of the system. However, reported systems still show limited mechanical stability, as expected from a PEG network, and this fact limits their potential application to load bearing tissues. Here, we describe mechanically reinforced PEG–catechol adhesives showing excellent and tunable cohesive properties and adhesive performance to tissue in the presence of blood. We used collagen/PEG mixtures, eventually filled with hydroxyapatite nanoparticles. The composite hydrogels show far better mechanical performance than the individual components. It is noteworthy that the adhesion strength measured on skin covered with blood was >40 kPa, largely surpassing (>6 fold) the performance of cyanoacrylate, fibrin, and PEG–catechol systems. Moreover, the mechanical and interfacial properties could be easily tuned by slight changes in the composition of the glue to adapt them to the particular properties of the tissue. The reported adhesive compositions can tune and improve cohesive and adhesive properties of PEG–catechol-based tissue glues for load-bearing surgery applications

The exploitation of easily accessible and nontoxic natural catechol compounds for surface functionalization and coating is attracting growing interest for biomedical applications. We report herein the deposition on different substrates of chemically stable thin films by autoxidation of 1 mM caffeic acid (CA) solutions at pH 9 in the presence of equimolar amounts of hexamethylenediamine (HMDA). UV–visible, mass spectrometric, and solid state 13C and 15N NMR analysis indicated covalent incorporation of the amine during CA polymerization to produce insoluble trioxybenzacridinium scaffolds decorated with carboxyl and amine functionalities. Similar coatings are obtained by replacing CA with 4-methylcatechol (MC) in the presence of HMDA. No significant film deposition was detected in the absence of HMDA nor by replacing it with shorter chain ethylenediamine, or with monoamines. The CA/HMDA-based films resisted oxidative and reductive treatments, displayed efficient Fe(II) and Cu(II) binding capacity and organic dyes adsorption, and provided an excellent cytocompatible platform for growing embryonic stem cells. These results pointed to HMDA as an efficient cross-linking mediator of film deposition from natural catechols for surface functionalization and coatings.

Cell adhesion is studied on multivalent knottins, displaying RGD ligands with a high affinity for integrin receptors, that are assembled on CB[8]-methylviologen-modified surfaces. The multivalency in the knottins stems from the number of tryptophan amino acid moieties, between 0 and 4, that can form a heteroternary complex with cucurbit[8]uril (CB[8]) and surface-tethered methylviologen (MV2+). The binding affinity of the knottins with CB[8] and MV2+ surfaces was evaluated using surface plasmon resonance spectroscopy. Specific binding occurred, and the affinity increased with the valency of tryptophans on the knottin. Additionally, increased multilayer formation was observed, attributed to homoternary complex formation between tryptophan residues of different knottins and CB[8]. Thus, we were able to control the surface coverage of the knottins by valency and concentration. Cell experiments with mouse myoblast (C2C12) cells on the self-assembled knottin surfaces showed specific integrin recognition by the RGD-displaying knottins. Moreover, cells were observed to elongate more on the supramolecular knottin surfaces with a higher valency, and in addition, more pronounced focal adhesion formation was observed on the higher-valency knottin surfaces. We attribute this effect to the enhanced coverage and the enhanced affinity of the knottins in their interaction with the CB[8] surface. Collectively, these results are promising for the development of biomaterials including knottins via CB[8] ternary complexes for tunable interactions with cells.